Formfutura Platinum SLA Series is a general-purpose photopolymer SLA resin that is specifically developed to work with all open source SLA, DLP, and LCD 3D Printers in the range of 385 – 405nm. Our Platinum SLA resin is almost odourless and 3D prints with and extremely high accuracy and a very smooth surface finish. 

 

 

Key features

  • High-resolution 3D printing with fine detail
  • Almost Odorless processing 
  • Excellent dimensional accuracy and low shrinkage
  • Low water absorption
  • Compatible with all open-source SLA, DLP, and LCD 3D printers in the range of 385 - 405nm 

 

Applications

  • Figurines and model
  • Functional prototyping
  • End-use products

 

Resin properties (uncured liquid)

  • Viscosity: 700 cps at 25°C
  • Density: 1.12 g/cm2

 

Mechanical properties

Test method on post cured objects through 30 minutes high power LED curing.

 

Properties

Typical Value

Test Method

Glass transition temperature (Tg)

54°C

ASTM D7028

Water absorption

0.3%

ASTM D570-98

Impact strength (IZOD notched)

15 J/m

ASTM D256A

Tensile strength

62 MPa

ASTM D638M

Tensile Modulus

2200 MPa

ASTM D638M

Elongation at break

4%

ASTM D638M

Flexural Strength

75 MPa

ASTM D790M

Flexural Modulus

1900 MPa

ASTM D2240

Shore D Hardness

78

ASTM D2240

 

 

Please note that the above-displayed values can vary with individual machine processing, post-curing parts,  geometry, print orientation, print settings, and temperature.

 

Preparation(s) before starting to print

  • Shake the bottle for at least 2 minutes before each use.
  • After shaking the bottle, leave the resin to rest for 10 minutes to let air bubbles get out of the resin
  • The resin can be poured back from the vat into the bottle once your print is finished
  • Always use protective measurements like safety glasses and nitrile gloves when handling resins.

 

Post-processing

  • We do advise you to post-process your 3D print in order to achieve the material properties
  • Rinse your 3D printed object in IPA or (Bio)Ethanol for approximately 5 minutes
  • Make sure that IPA and/or (Bio)Ethanol rinsed objects are perfectly dry before further post-curing
  • Cure your object in a high power curing chamber for approximately 20-30 minutes at 65° C
  • An ultrasonic cleaner is preferred/recommended
  • Place the rinsed parts in a well-ventilated area for at least 30 minutes, or use pressurized air for at least 2 minutes
  • The preferred curing wavelength is between 300-410nm

 

Safety

Please always be aware that when 3D printing with resins that you are working with chemicals and that you should always be cautious and use the personal protective equipment as stipulated in our safety data sheets.

  • Always wear Respiratory Protection when sanding/cutting the resin object.
  • Always use nitrile gloves when handling resins and uncured resin objects.

 

Product export information

HS Code: 2916140090

Description: Resin for 3D printing

Country of origin: the Netherlands